CHI MEI CORPORATION
壓克力粒
ACRYREX
|
|
物性
|
ASTM TEST METHOD
|
CM-205
|
CM-207
|
CM-211
|
|
物理性質
PHYSICAL PROPERTIES
|
|
比重
|
D-792
|
1.19
|
1.19
|
1.19
|
|
流動系數
|
D-1238 gm/10min
|
1.8
|
8
|
16
|
|
假密度
|
D-1182 gm/cm3
|
0.77
|
0.77
|
0.77
|
|
成型收縮率
|
D-955 mm/mm
|
.002-.006
|
.002-.006
|
.002-.006
|
|
硬度
|
D-785
|
M-95
|
M-85
|
M-84
|
|
吸水率
|
D-570 %
|
0.3
|
0.3
|
0.3
|
|
燃燒率
|
UL-94
|
1/16"HB
|
1/16"HB
|
1/16"HB
|
|
光學性質
OPTICAL PROPERTIES
|
|
曲折率
|
D-542
|
1.491
|
1.491
|
1.491
|
|
全光透過率
|
D-1003 %
|
92
|
92
|
92
|
|
機械性質
MECHANICAL PROPERTIES
|
|
引張強度
|
D-638 (PSI)/( kg/cm2)
|
10200
|
720
|
9700
|
680
|
9200
|
650
|
|
彎曲強度
|
D-790 (PSI)/( kg/cm2)
|
15600
|
1100
|
14200
|
1000
|
13200
|
930
|
|
延伸率
|
D-638 %
|
5.0
|
5.0
|
5.0
|
|
抗衝擊力
|
D-256 (ft-lbs/in2)/(kg-cm/cm)
|
0.37/2.0
|
0.37/2.0
|
0.37/2.0
|
|
熱性質
THERMAL PROPERTIES
|
|
熱變形溫度
|
D-648
|
。C/。F
|
100/212
|
92/198
|
90/194
|
|
軟化點
|
D-1525
|
。C/。F
|
113/235
|
105/221
|
102/216
|
|
電氣性質
ELECTRICAL PROPERTIES
|
|
絕緣耐力
|
D-149 Volts/Mil
|
500
|
500
|
500
|
|
誘電率
|
D-150-647b
|
3.7
|
3.7
|
3.7
|
|
誘電率力
|
D-150-647
|
0.5
|
0.5
|
0.5
|
|
失電率
|
D-150
|
0.19
|
0.19
|
0.19
|
|
體積固有抵抗
|
D-257 Ωcm
|
1015
|
1015
|
1015
|
| |
|
|
|
|
|
|
|
|
|
|
CHI MEI CORPORATION
ABS CHARACTERISTIC
POLYLAC
|
|
特性
|
試驗法
|
Unit
|
一般級-1
|
|
PA-707
|
PA-757
|
PA-717C
|
|
|
引張強度
|
D-638
|
kg/cm2
|
500
|
480
|
450
|
|
|
(lb/in2)
|
7090
|
6800
|
6380
|
|
|
延伸率
|
D-638
|
%
|
15
|
20
|
25
|
|
|
彎曲彈性率
|
D-790
|
104 kg/cm2
|
2.9
|
2.7
|
2.5
|
|
|
(105lb/in2)
|
(4.1)
|
(3.8)
|
(3.5)
|
|
|
彎曲強度
|
D-790
|
kg/cm2
|
860
|
790
|
720
|
|
|
(lb/in2)
|
(12,200)
|
(11,200)
|
(10,200)
|
|
|
洛氏硬度
|
D-785
|
R-116
|
R-116
|
R-115
|
|
|
IZOD
衝擊強度
|
D-256
|
1/8"kg-cm/cm
|
16
|
20
|
28
|
|
|
(ft-lb/in)
|
(2.9)
|
(3.7)
|
(5.2)
|
|
|
1/4"kg-cm/cm
|
14
|
18
|
25
|
|
|
(ft-lb/in)
|
(2.6)
|
(3.3)
|
(4.6)
|
|
|
軟化點
|
D-1525
|
℃
|
105
|
105
|
104
|
|
|
(℉)
|
(221)
|
(221)
|
(219)
|
|
|
熱變形溫度
|
D-648
|
退火
|
℃(℉)
|
99(210)
|
99(210)
|
98(208)
|
|
|
未退火
|
℃(℉)
|
88(190)
|
88(190)
|
87(189)
|
|
|
比重
|
D-792
|
23/23℃
|
1.06
|
1.05
|
1.04
|
|
|
流動係數
|
D-1238
|
200℃, 5kg
g/10min
(Cond.G)
|
1.9
|
1.8
|
1.4
|
|
|
ISO-1133*
|
220℃, 10kg
g/10min
|
20
|
22
|
15
|
|
|
燃燒率
|
File No.
E56070
UL & C-UL
|
1/16"HB
|
1/16"HB
|
1/16"HB
|
|
|
產品特性
|
高光澤性
高剛性
|
高剛性
高光澤性
|
一般射出
成型用
|
|
|
CHI MEI CORPORATION
PS CHARACTERISTIC
POLYREX
|
|
特性
|
試驗法
|
單位
|
耐衝擊級
|
|
PH-60
|
PH-60C
|
PH-88
|
PH-88H
|
PH-888H
|
|
引張強度
|
D-638
|
kg/cm2
|
280
|
270
|
250
|
270
|
300
|
|
(lb/in2)
|
(3,970)
|
(3,830)
|
(3,550)
|
(3,830)
|
(4,260)
|
|
延伸率
|
D-638
|
%
|
40
|
35
|
40
|
40
|
45
|
|
彎曲彈性率
|
D-790
|
104 kg/cm2
|
2.2
|
2.3
|
2.0
|
2.0
|
2.0
|
|
(105 lb/in2)
|
(3.1)
|
(3.3)
|
(2.8)
|
(2.8)
|
(2.8)
|
|
彎曲強度
|
D-790
|
kg/cm2
|
430
|
430
|
380
|
450
|
450
|
|
(lb/in2)
|
(6,110)
|
(6,110)
|
(5,400)
|
(6,390)
|
(6,390)
|
|
洛氏硬度
|
D-785
|
L-87
|
L-85
|
L-75
|
L-77
|
L-80
|
|
IZOD
衝擊強度
|
D-256
|
1/8" kg-cm/cm
|
8.5
|
8.0
|
11.0
|
10.0
|
9.0
|
|
(ft-lb/in)
|
(1.56)
|
(1.46)
|
(2.02)
|
(1.84)
|
(1.65)
|
|
1/4" kg-cm/cm
|
7.5
|
7.0
|
9.0
|
8.5
|
7.5
|
|
(ft-lb/in)
|
(1.38)
|
(1.28)
|
(1.65)
|
(1.56)
|
(1.38)
|
|
軟化點
|
D-1525
|
℃
|
100
|
95
|
99
|
102
|
102
|
|
(℉)
|
(212)
|
(203)
|
(210)
|
(215)
|
(215)
|
|
熱變形溫度(未退火)
|
D-648
|
℃
|
86
|
80
|
82
|
85
|
85
|
|
(℉)
|
(186)
|
(176)
|
(180)
|
(185)
|
(185)
|
|
比重
|
D-792
|
23/23。C
|
1.05
|
1.05
|
1.05
|
1.05
|
1.05
|
|
流動係數
|
D-1238
|
(Cond.G) g/10min
|
5.5
|
8.5
|
5.0
|
4.7
|
3.8
|
|
(Cond.I) g/10min
|
16.0
|
23.0
|
15.0
|
14.5
|
10.8
|
|
燃燒率
|
File No.
E56070
UL & C-UL
|
1/16"HB
|
1/16"HB
|
1/16"HB
|
1/16"HB
|
1/16"HB
|
|
產品特性
|
耐熱中衝擊級
|
磁碟片專用
|
高衝擊級射出成型
|
耐熱高衝擊級
|
耐熱高落下衝級
|
|
CHI MEI CORPORATION
ABS CHARACTERISTIC
POLYLAC
|
|
特性
|
試驗法
|
單位
|
防火級-1
|
|
PA-766
|
PA-765
|
PA-765A
|
PA-765B
|
|
引張強度
|
D-638
|
kg/cm2
|
380
|
390
|
400
|
400
|
|
(lb/in2)
|
(5,400)
|
(5,530)
|
(5,670)
|
(5,670)
|
|
延伸率
|
D-638
|
%
|
30
|
15
|
15
|
25
|
|
彎曲彈性率
|
D-790
|
104kg/cm2
|
2.0
|
2.1
|
2.3
|
2.4
|
|
(105lb/in2)
|
(2.8)
|
(3.0)
|
(3.2)
|
(3.4)
|
|
彎曲強度
|
D-790
|
kg/cm2
|
590
|
620
|
640
|
650
|
|
(lb/in2)
|
(8,360)
|
(8,800)
|
(9,070)
|
(9,200)
|
|
洛氏硬度
|
D-785
|
R-95
|
R-100
|
R-100
|
R-102
|
|
IZOD
衝擊強度
|
D-256
|
1/8"kg-cm/cm
|
23
|
22
|
24
|
26
|
|
(ft-lb/in)
|
(4.3)
|
(4.0)
|
(4.4)
|
(4.8)
|
|
1/4"kg-cm/cm
|
21
|
18
|
20
|
22
|
|
(ft-lb/in)
|
(3.9)
|
(3.3)
|
(3.7)
|
(4.0)
|
|
軟化點
|
D-1525
|
℃
|
98
|
90
|
92
|
95
|
|
(℉)
|
(214)
|
(194)
|
(197)
|
(203)
|
|
熱變形溫度
|
D-648
|
退火
|
℃(℉)
|
89(192)
|
83(181)
|
85(185)
|
86(187)
|
|
未退火
|
℃(℉)
|
81(178)
|
73(165)
|
76(179)
|
79(174)
|
|
比重
|
D-792
|
23/23℃
|
1.20
|
1.19
|
1.17
|
1.16
|
|
流動係數
|
D-1238
|
200℃, 5kg
g/10min
(Cond.G)
|
2.3
|
5.2
|
4.8
|
4.2
|
|
ISO-1133*
|
220℃, 10kg
g/10min
|
25
|
60
|
48
|
42
|
|
燃燒率(*)
|
File No.
E56070
UL & C-UL
|
1/16" V-O
|
1/16" V-O
1/10" 5VA
|
1/12" V-O
1/10" 5VA
|
1/10" V-O
1/16" V-2
1/8" 5VA
|
|
產品特性
|
難燃性
耐熱性
高衝級
|
難燃性
耐光性
|
難燃性
耐光性
|
難燃性
耐光性
耐熱性
|
|
| |
|